lThe effect of the effective threading length of the standardized thread on the bolt tensile test results Tan Xiaozhou (Hubei Sanjiang Aerospace Insurance Peak Electronic Information Co., Ltd., Xiaogan 432009) analyzed the relevant procedures and found that the "thread effective stitching length" is the key to the test results. One of the factors. The maximum value is not required in the standard, which may result in distortion of the thread load capacity test results.
Ability level. The specific method is as follows: (L is the effective screw length of the thread, F is the tensile force), fix the bolt head, screw the threaded end of the bolt into the internal thread clamp, and apply the tensile force corresponding to the performance level in the longitudinal direction (minimum Pull load). When the force value arrives, the bolt must not trip and break.
Bolts (including screws, studs, the same below) in the product structure, play the role of connection, fixation and reinforcement, its bearing capacity is directly related to the stability and reliability of the product structure. When the bolt is in use, its head, the rod and the threaded end serve as a load. In order to determine whether each part meets the requirements, the most direct test method is to carry out the tensile test of the bolt. The tensile test procedure in GB/T3098.1-2010 specifies the minimum value of the effective screw length of the thread, but does not require a maximum value. After analysis, the author believes that when the effective screwing length of the thread exceeds a certain limit, the force receiving area of ​​the thread in the loading fixture increases, and the stress is correspondingly reduced, so that some thread quality defects and hidden dangers which can be found in the tensile test are therefore caused. It is hidden, causing the test results to differ from the real situation.
1 Bolt force analysis in the tensile test 1.1 Bolt tensile test test method By simulating the actual use of the bolt, the rated force value is applied, and the bolt deformation is observed to determine whether it has achieved self-standardity. The thread diameter cross-sectional area is the main body that bears the stress, and the thread that is not screwed into the internal thread clamp part can be regarded as the extension of the external thread small diameter. The bottom width P is integrated with the external thread small diameter to support the bolt and resist the deformation of the force. Made a certain contribution.
2 Influence of effective thread length on the tensile test results 2.1 Relationship between effective thread length and shear stress The above analysis shows that the effective screw length determines the stress area subjected to shear stress F. Under the condition that the shear stress F (ie, the minimum tensile load of the test tension) is constant, the effective screwing length of the thread is proportional to the stress area subjected to the shear stress F, and inversely proportional to the shear stress on the area.
2.2 Test Verification of the Effect of Thread Effective Thread Length on Tensile Test Results In order to verify whether the above analysis conclusions are correct, the author designed and implemented a group test. Of the same batch of screws that were qualified for mechanical properties and dimensional measurements, five were randomly selected as test samples.
The slotted cylindrical head screw specified in 65-2000 is M6mmX25mm, the pitch is 1mm, the performance grade is 4.8, and the minimum tensile load is 8440N. Five full-thread screw samples are screwed into the internal thread clamp with different effective screw lengths, and the tension is applied. The load does not fail until it breaks. The hardness of the internal thread clamp is 55HRC, and the tensile speed is min-1. The test results are shown in Table 1. Table 1 The effect of the effective screw length of the thread on its bearing capacity Tab.1Influencesofeffectivelengthsof screw number screwing depth screwing buckle number of tensile load failure state The unspinned part of the trip is broken. Note: 1) A nut equivalent to a nominal height of 0.5 D, a thread effective length of 0.4 D; 2) a nut equivalent to a nominal height of 0.8 D and an effective thread length of 0.6 D.
Shi Xia et al: Analysis of the cause of the breakage of the engine cylinder head bolts The tensile stress causes delayed fracture of the bolt.
From the above analysis, it can be concluded that the hydrogen embrittlement fracture of the bolt occurs under the joint action of hydrogen, material microcrack and tensile stress. First, excess hydrogen is the most basic cause of hydrogen embrittlement fracture of bolts.
For bolts with a strength greater than 1200 MPa, the hydrogen content of the material at 5X10610X106 can cause hydrogen embrittlement. According to the mechanical property test and the dehydrogenation test, the strength of the fracture bolt is 1260 MPa, which is a high-strength bolt, has high hydrogen embrittlement sensitivity, and excess hydrogen is retained in the fracture bolt. From the point of view of the bolt production process, the high hydrogen content should be caused by surface phosphating or dehydrogenation. Secondly, the existence of microcracks and residual stress in the bolt material is a necessary condition for accelerating hydrogen accumulation, diffusion and even fracture. The external condition in which the bolt is hydrogen embrittled is that the bolt is subjected to static tensile stress. According to the above calculation, the tensile stress after the bolt assembly is about 544 MPa, and the hydrogen brittle stress strength of the bolt is 376 MPa, so that the bolt is assembled with delayed fracture under the action of hydrogen.
3 Conclusions and recommendations (1) The hydrogen brittle fracture occurs in the bolt. The reason is that the residual hydrogen in the surface phosphating and dehydrogenation process enters the surface of the bolt. Under the action of tensile stress during assembly, the bolt produces hydrogen embrittlement crack and Eventually a hydrogen embrittlement fracture occurs.
Grade 9, with high hydrogen embrittlement sensitivity. Therefore, in the bolt production process, especially in the surface treatment process, the process documentation must be strictly implemented to ensure complete hydrogen removal. It is necessary to strengthen the hydrogen embrittlement sensitivity test of bolts after hydrogen removal to avoid hydrogen embrittlement.
The RFID Seal tags is one way lock, can open it one lock unless damage it.
Industrial level material, ABS or PPS, waterproof, high temperature resistance.
And pupular using in trees management, assesses management, water meter and pipeline management etc. Any hard working environment, it is a great option.
You logo or variable numbers would be laser printed on the rfid seal surface, making the management more easy.
RFID Seal Tag can be embedded 125Khz chips like Tk4100, EM4200, T5577, EME44305 and Hitag etc.
RFID Seal Tag can be embedded 13.56MHZ chips like Ntag213, NTAG215, NTAG216, Mifare Classic, Desfire EV2/EV2, Plus X, Plus SE, ICODE, Ultralight, TI 2084, Topaz512, and F08 etc.
RFID seal tag can be embedded 860MHZ-960MHZ chips like Alien H3, Alien H4, U-Code Gen2 and Impinj M4/M5 etc.
Besides, SunwayRFID also provides silicone rfid wristband, rifd bracelet, Elastic Wristband, snap wristband, Fabric Wristbands, pvc wristbands, RFID Keychain, RFID Tag and rfid cards too, one-shop can meet all your need about RFID.
Price, customer service, and quality always at our first place.
RFID Seal Tag
RFID Seal Tag,Seal Tag,RFID Seal,Plastic Seal Tag
Sunway Smartech Co.,LTD , https://www.sunwayrfid.com